18-10-2007, 05:48 PM
aimre

This site stresses me out
18-10-2007, 06:15 PM
aaronng

Weq's method works great. Go for that.
18-10-2007, 08:36 PM
Sexc86

Quote:

Originally Posted by Weq

Go pay 200 for your JDM (y0!) anodized blinging cooler.

AHAHAH Yo! That is 'Gansta'
19-10-2007, 05:18 PM
Limbo

i sprayed my oil cooler with HT paint no issues at all.
24-10-2007, 07:07 PM
kraiye

heat transferring paint like radiator paint will be the best cheaper option

and why aren't there anodised IC's readily available... I'm sure there'd be a big market for it, and not just black but red, blue, custom colour lol etc etc
24-10-2007, 10:35 PM
aimre

Quote:

Originally Posted by kraiye

heat transferring paint like radiator paint will be the best cheaper option

and why aren't there anodised IC's readily available... I'm sure there'd be a big market for it, and not just black but red, blue, custom colour lol etc etc

Becoz most people arent stooges like on this site and will just pay the extra $3 and spray paint there own.

Why pay an extra 50-100$ for anondizing?

Do u think anondizing wont effect its thermal properties????

Quote:

Originally Posted by Edwards, Joseph (1997).***

Anodized coatings have a much lower thermal conductivity and coefficient of linear expansion than aluminum. As a result, they will crack if exposed to temperatures above 80°C, although they will not peel.

F*ck this site is full of morons who dont ever listen.

*** Edwards, Joseph (1997). Coating and Surface Treatment Systems for Metals. Finishing Publications Ltd. and ASM International, pp. 34-38.
24-10-2007, 10:40 PM
SLOWEGG

Quote:

Originally Posted by aimre

Becoz most people arent stooges like on this site and will just pay the extra $3 and spray paint there own.

Why pay an extra 50-100$ for anondizing?

Do u think anondizing wont effect its thermal properties????

F*ck this site is full of morons who dont ever listen.

*** Edwards, Joseph (1997). Coating and Surface Treatment Systems for Metals. Finishing Publications Ltd. and ASM International, pp. 34-38.

Lol..
25-10-2007, 07:38 AM
dsp26

Quote:

Originally Posted by Limbo

i'm sure a light coat will not effect the cooling to any noticable degree, but use HT paint as it is better quailty and does not flake of as easily

yeah that was my point.. it sticks differently than normal point and is a lot thinner therefore it won't reduce the thermal efficiency as much as paint. reason i mentioned painting headers with them is to back up the fact that they do not peel under extreme heat therefore would possibly be suitable for ICs as they cannot possibly get as hot or hotter... can they?

BUT then again i know nothing of both paints chemical composition and thermal effects to make that call... visually the idea is quite sound
25-10-2007, 09:16 PM
kraiye

Quote:

Originally Posted by aimre

Becoz most people arent stooges like on this site and will just pay the extra $3 and spray paint there own.

Why pay an extra 50-100$ for anondizing?

Do u think anondizing wont effect its thermal properties????

F*ck this site is full of morons who dont ever listen.

*** Edwards, Joseph (1997). Coating and Surface Treatment Systems for Metals. Finishing Publications Ltd. and ASM International, pp. 34-38.

would you like a tissue for those tears?

sorry man but you whinge a lot... every one's a moron/stooge... no one listens... blah blah bleat bleat. go grab a razor, put on some panic and end it all now before the pain becomes too unbearable
26-10-2007, 12:15 AM
aimre

I called you morons, the rest of my post was facts... Not really whinging
26-10-2007, 01:26 AM
aimre

Quote:

Originally Posted by kraiye

would you like a tissue for those tears?

sorry man but you whinge a lot... every one's a moron/stooge... no one listens... blah blah bleat bleat. go grab a razor, put on some panic and end it all now before the pain becomes too unbearable

and idk if u noticed, but im mostly trying to save you people money
29-10-2007, 07:08 PM
kraiye

Quote:

Originally Posted by aimre

and idk if u noticed, but im mostly trying to save you people money

dont get me wrong, i respect your responses especially when based on knowledge and experience unlike other 'stooges'... just remember though it isn't a professionals forum and people are always gonna put it their 2c, and not everyone knows who to listen to.

i really do think it's good you can give solid advice, i just enjoy watching the way you go about it

:thumbsup: